For HIP ( Hot
Isostatic Pressing ) |
|
|
Characteristics
|
|
|
Highly spherical alloy powders made by high-pressure water jet
spray on inert gas on molten metal.
Slow solidification in long chamber being possible, the in-mixing of irregular and leaf-shape powders is
minimised. |
|
|
|
Example for Range of Particle Sizes
|
|
|
|
Example for Chemical Compositions of
Powder
|
| Daido
Bland |
Chemical Compositions (mass%) |
Similar
Steel Type
HRC |
|
C |
Ni |
Cr |
Mo |
W |
V |
Co |
| DAP520 |
1.30 |
|
4.0 |
5.0 |
6.5 |
3.0
|
|
|
| DAP540 |
1.30 |
|
4.0 |
5.0 |
6.5 |
3.0 |
8.0 |
|
| DAPMH51 |
0.85 |
|
4.2 |
5.0 |
6.0 |
3.0 |
|
|
| DAPDC11 |
1.50 |
|
12.0 |
1.0 |
|
0.3 |
|
|
| DAPDHA1 |
0.37 |
|
5.0 |
1.25 |
|
1.0 |
|
|
| DAPKCW1 |
2.50 |
|
30.0 |
|
12.0 |
|
Bal. |
|
| DAPKCW2 |
1.20 |
|
30.0 |
|
4.0 |
|
Bal. |
|
| DAPKCW3 |
1.50 |
|
30.0 |
|
8.0 |
|
Bal.
|
|
| DAPKCM1 |
0.25 |
3.0 |
26.0 |
5.5 |
|
|
Bal.
|
|
| DAPKCN1 |
|
|
|
|
|
|
|
|
| DAPK625 |
|
Bal. |
21.5 |
9.0 |
Nb5.0 |
|
|
|
| DAPRC276 |
|
|
|
|
|
|
|
|
*Products
with particle-size and chemical composition other than
those shown
above may be available upon consultation |
|
|
|
|
|
|